Zinc-oxide nanowires electrochemically grown onto sol-gel spin-coated seed layers

Claudia D. Bojorge, Vladimir R. Kent, Erika Teliz, Horacio R. Cánepa, Rodrigo Henríquez, Humberto Gõmez, Ricardo E. Marotti, Enrique A. Dalchiele

Resultado de la investigación: Contribución a una revistaArtículorevisión exhaustiva

33 Citas (Scopus)

Resumen

The electrochemical deposition of ZnO nanowires (NW) was optimized by growing onto a previously deposited seed layer. The ZnO seed layer was prepared by a sol-gel process from different precursor solutions and deposited onto FTO/glass by spin coating. Afterwards, NW were electrochemically grown onto those seed layers. The electrolyte was an aqueous solution of the Zn +2 precursor (1 mM zinc acetate) and a supporting electrolyte (0.1 M sodium acetate), saturated with bubbling oxygen. The films were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), and optical transmittance. The XRD measurements show typical diffraction pattern of ZnO wurtzite structure. The SEM micrographs show the presence of smooth NW with hexagonal sections with diameters ranging from 40 to 250 nm. The optical transmittance reveals the presence of ZnO with bandgap energy between 3.23 and 3.29 eV. These spectra show a monotonically increasing transmittance from the UV into the red part of the spectrum. This feature may be originated in the dispersion of light at the NW and can be used to enhance below-gap absorption.

Idioma originalInglés
Páginas (desde-hasta)1662-1669
Número de páginas8
PublicaciónPhysica Status Solidi (A) Applications and Materials Science
Volumen208
N.º7
DOI
EstadoPublicada - jul 2011
Publicado de forma externa

Huella

Profundice en los temas de investigación de 'Zinc-oxide nanowires electrochemically grown onto sol-gel spin-coated seed layers'. En conjunto forman una huella única.

Citar esto